Hybrid HM
Single-component, hybrid polymer-based adhesive-sealant with anti mould agent for overpaintable elastic bonding and sealing of joints in construction and industry in general.
Single-component, hybrid polymer-based adhesive-sealant with anti mould agent for overpaintable elastic bonding and sealing of joints in construction and industry in general.
Single-component, hybrid polymer-based adhesive-sealant with anti mould agent for overpaintable elastic bonding and sealing of joints in construction and industry in general.
- Overpaintable
- Suitable for indoor and outdoor use, also on moist substrates
- Ideal for both construction and industry
- Very low emissions of Volatile Organic Compounds
Variations
Choose the perfect solution for your project
White 9016
Grey 7004
Black 9005
Crystal clear
Application areas
Where Hybrid HM performs best
Discover more
Other solutions you might be interested in
Mirror
Neutral silicone adhesive for bonding mirrors.
Neutral silicone adhesive for bonding mirrors.
Sitol® Primer Glass
Primer formulated as a black pre-treatment for glass surfaces to…
Primer formulated as a black pre-treatment for glass surfaces to provide a protective coating against UV radiation.
Sitol® Deck Bonding LV
Low viscosity hybrid adhesive for bonding natural and synthetic teak…
Low viscosity hybrid adhesive for bonding natural and synthetic teak decks. Suitable for large surfaces.
Sitol® M.E.D.
A high-performance structural adhesive and hybrid sealant for all types…
A high-performance structural adhesive and hybrid sealant for all types of applications in the marine industry specifically formulated for bonding and sealing mineral and organic glass.
Sitol® Meta 45
A two-component, methacrylate-based structural adhesive with excellent thixotropic properties that…
A two-component, methacrylate-based structural adhesive with excellent thixotropic properties that enable the creation of vertical lines without dripping and medium curing time.
Adhesive for EPDM membrane
High-viscosity adhesive for the façade application of EPDM membrane on…
High-viscosity adhesive for the façade application of EPDM membrane on vertical and horizontal surfaces.
Sitol® Infinity
Fast curing hybrid adhesive and sealant suitable for wet surfaces.
Fast curing hybrid adhesive and sealant suitable for wet surfaces.
Sitol® Primer Deck Caulking
Primer for sealants on wooden and porous substrates.
Primer for sealants on wooden and porous substrates.
Sitol® Deck Caulking S
Neutral, sandable silicone sealant for teak caulking.
Neutral, sandable silicone sealant for teak caulking.
Sitol® Deck Bonding
Hybrid polymer-based adhesive-sealant with extended open time for natural and…
Hybrid polymer-based adhesive-sealant with extended open time for natural and synthetic teak.
Sitol® Deck Caulking
Hybrid polymer-based, sandable sealant for teak caulking.
Hybrid polymer-based, sandable sealant for teak caulking.
Sitol® Marine
Fast hardening adhesive-sealant based on hybrid polymers with high initial…
Fast hardening adhesive-sealant based on hybrid polymers with high initial adhesion.
Details
Hybrid HM is a high-quality, professional adhesive-sealant based on hybrid polymers, which cures by reaction with moisture to form a permanently elastic mass that does not shrink or swell. It absorbs vibrations and acoustically insulates bonded elements. The presence of an anti-microbial and anti-algal agent in the formulation makes it suitable for use in sanitary environments. It is also resistant to UV rays, ageing in general, chemical agents and water stagnation. It adheres to all typical building and industrial materials, natural and synthetic, smooth and porous, even wet, provided they are clean, degreased and compact. It does not produce substances that can corrode metal substrates and does not develop unpleasant odours. It is free of solvents and isocyanates. The product is certified as EC1 Plus by the GEV organisation in terms of very low emissions of volatile organic substances.
Instructions for use
Use as a sealant:
- The joint flanks must be solid, clean, degreased and consistent.
- Insert the Synthetic Plugging Cord to ensure the correct proportioning of the sealant and non-adhesion at the bottom of the joint.
- Protect the edges of the joint with self-adhesive paper tape.
- Cut the nozzle to a diameter proportional to the joint size.
- Inject an excess amount of Hybrid HM.
- Smooth with a small spatula moistened with Smooth smoothing agent before surface filming begins. Apply pressure so that the sealant fills without voids and completely adheres to the joint flanks.
- Remove the protective tape immediately.
Use as an adhesive:
- Surfaces must be solid, clean, degreased and consistent.
- Insert the cartridge/bag into the cartridge gun, open it, screw on the nozzle and cut it according to the quantity to be extruded.
- Spread the adhesive with a suitable notched trowel in sufficient quantity to cover the bonding area.
- To ensure adequate elasticity of the adhesive layer, apply a thickness of 2 mm.
- Bring the materials into position and glue before spinning the surface.
- Fasten the bodies externally to support their weight during the first 24 hours.
Cleaning the tools
Clean tools with paper and alcohol while Hybrid HM is still fresh, mechanically after curing.
Storage
Store in a dry place, protected from frost and heat. In the original unopened packaging and protected from UV rays it will keep for at least 12 months.
Warnings
- Do not apply at temperatures below 0 °C.
- Do not use in constantly wet environments, in continuous contact with water or chlorine.
- Extended exposure to UV rays may cause yellowing.
- In the case of application on plastic or otherwise dubious substrates, check the adhesion of Hybrid HM with preliminary tests.
- Clean tools with paper and alcohol while Hybrid HM is still fresh, mechanically after curing.
- Not suitable for: PE, PP, PMMA, PTFE, polycarbonate, soft plastics, neoprene and bituminous surfaces.
| Color | Code | Packaging | Packaging size | Pallet | Barcode |
|---|---|---|---|---|---|
| White 9016 | 5665 | cartridge | 12x290 ml |
116 cardboards
|
|
| Grey 7004 | 5666 | cartridge | 12x290 ml |
116 cardboards
|
|
| Black 9005 | 5667 | cartridge | 12x290 ml |
116 cardboards
|
|
| White 9016 | 5513 | foil bag | 20x600 ml |
36 cardboards
|
|
| Grey 7004 | 5514 | foil bag | 20x600 ml |
36 cardboards
|
|
| Black 9005 | 5512 | foil bag | 20x600 ml |
36 cardboards
|
|
| Crystal clear | 8037 | cartridge | 12x290 ml |
116 cardboards
|
|
Joints between construction elements, vertical and horizontal. Once hardened, it can be painted over and, in its crystalline form, it is completely transparent. It guarantees good weather resistance and excellent adhesion to smooth and porous surfaces, even damp ones, provided they are free of grease and dust: glass, rigid plastics, metal substrates, plasterboard, masonry, wood, fibre cement boards, etc. It does not corrode metals, does not reduce its initial volume and retains its elasticity even at low temperatures without stressing the joint flanks. It is also particularly suitable for high-strength bonding of elements subject to thermal expansion or mechanical vibration/stress.
| PARAMETER AND TEST METHOD | WHITE, GREY, BLACK | CRYSTAL CLEAR |
| Density (UNI 8490 – Part 2^) | 1,428 g/ml | 1,057 g/ml |
| Extrusion speed (MIT 30) | 29 g | 40,79 g |
| Application temperature | +5 °C to +30 °C | +5 °C to +30 °C |
| Skin-over time (MIT 33) | 20 minutes | 10 minutes |
| Curing speed (+23 °C – 50% r.h.) | 2-3 mm/24 h | 4 mm/24 h |
| Slip resistance (EN ISO 7390) | ≤ 3 mm | ≤ 3 mm |
| Operating temperature | -30 °C to +80 °C | -30 °C to +80 °C |
| Surface hardness Shore A (ISO 868) | 47 | 35 ± 5 |
| Variation in volume (MIT 057) | 3,2% | 3,5% |
| Mass variation (MIT 057) | 1,8% | 2,6% |
| Elongation to break (DIN 53504 – S2) | 390% | 300% |
| Tensile load at break (DIN 53504 – S3A) | 1,46 MPa | – |
| Tensile load at break (DIN 53504 – S2) | – | 2,4 MPa |
| Modulus of elasticity at 100% (DIN 53504 – S3A) | 0,83 MPa | – |
| Modulus of elasticity at 100% (DIN 53504 – S2) | – | 0,9 MPa |
| Maximum operating elongation (ISO 11600) | 20% | 7,5% |
Indicative yield in running metres of one cartridge/foil bag of sealant = V / ( L x P).
V = Cartridge/bag content in ml
L = Sealing width in mm
P = Sealing depth in mm
When applied with a notched trowel as an adhesive, consumption varies depending on the roughness of the substrate.
The estimated bonding surface area with one cartridge is 0.33 m²; with one bag, 0.68 m² (approximately 875 ml/m²).