AF 2.0
Single-component acrylic-based elasto-plastic sealant in aqueous dispersion for overpaintable sealing of cracks, fissures and connection joints between façade elements with a maximum working elongation of 7.5%.
Single-component acrylic-based elasto-plastic sealant in aqueous dispersion for overpaintable sealing of cracks, fissures and connection joints between façade elements with a maximum working elongation of 7.5%.
- Can be painted after 20 minutes
- Rapid surface film formation
- Elastic elongation 7.5%
- Very low emissions of volatile organic compounds
Discover more
Other solutions you might be interested in
Mirror
Neutral silicone adhesive for bonding mirrors.
Neutral silicone adhesive for bonding mirrors.
Sitol® Primer Glass
Primer formulated as a black pre-treatment for glass surfaces to…
Primer formulated as a black pre-treatment for glass surfaces to provide a protective coating against UV radiation.
Sitol® Deck Bonding LV
Low viscosity hybrid adhesive for bonding natural and synthetic teak…
Low viscosity hybrid adhesive for bonding natural and synthetic teak decks. Suitable for large surfaces.
Sitol® M.E.D.
A high-performance structural adhesive and hybrid sealant for all types…
A high-performance structural adhesive and hybrid sealant for all types of applications in the marine industry specifically formulated for bonding and sealing mineral and organic glass.
Sitol® Meta 45
A two-component, methacrylate-based structural adhesive with excellent thixotropic properties that…
A two-component, methacrylate-based structural adhesive with excellent thixotropic properties that enable the creation of vertical lines without dripping and medium curing time.
Adhesive for EPDM membrane
High-viscosity adhesive for the façade application of EPDM membrane on…
High-viscosity adhesive for the façade application of EPDM membrane on vertical and horizontal surfaces.
Sitol® Infinity
Fast curing hybrid adhesive and sealant suitable for wet surfaces.
Fast curing hybrid adhesive and sealant suitable for wet surfaces.
Sitol® Primer Deck Caulking
Primer for sealants on wooden and porous substrates.
Primer for sealants on wooden and porous substrates.
Sitol® Deck Caulking S
Neutral, sandable silicone sealant for teak caulking.
Neutral, sandable silicone sealant for teak caulking.
Sitol® Deck Bonding
Hybrid polymer-based adhesive-sealant with extended open time for natural and…
Hybrid polymer-based adhesive-sealant with extended open time for natural and synthetic teak.
Sitol® Deck Caulking
Hybrid polymer-based, sandable sealant for teak caulking.
Hybrid polymer-based, sandable sealant for teak caulking.
Sitol® Marine
Fast hardening adhesive-sealant based on hybrid polymers with high initial…
Fast hardening adhesive-sealant based on hybrid polymers with high initial adhesion.
Details
Instructions for use
The sides of the joint must be solid, clean and consistent. The dimensions of the sealing must be minimum 6 x 6 mm and maximum 25 x 12.5 mm. On deep expansion joints, insert the backfill sealant. AF 2.0 does not require primer: on very absorbent substrates, first apply AF 2.0 diluted with water with a brush. Cut the nozzle according to a diameter proportional to the size of the joint. Inject an excess amount of AF 2.0. Smooth out with a spatula dampened with “Smooth” smoothing agent before the surface film formation begins. Apply a certain pressure in order to obtain a void-free filling and complete adhesion of the sealant on the sides of the joint.
Storage
Store in a dry, heat-protected place. In the original packaging it is kept for at least 18 months.
Warnings
- Not suitable for sealing that can be walked on or constantly exposed to water.
- Do not apply on unpainted ferrous surfaces.
- Do not apply in case of risk of rain.
- Do not store or apply at temperatures below 0 °C.
- Clean tools with water AF 2.0 is still fresh; mechanically and with organic solvents if hardened.
| Color | Code | Packaging | Packaging size | Pallet | Barcode |
|---|---|---|---|---|---|
| White | 8029 | cartridge | 24x310 ml |
60 cardboards
|
|
For applications on joints between vertical or horizontal construction elements subject to low stress, as long as there is no continuous water stagnation. Can be painted after 20 minutes (a preliminary test is recommended). Excellent adhesion on porous substrates, even damp ones: plasterboard, plaster, masonry, wood, fibre cement, concrete.
| TEST PARAMETER AND METHOD | VALUE |
| Density (UNI 8490 – Part 2^) | 1,655 g/ml |
| Extrusion speed (MIT 30) | 62,21 g |
| Application temperature | from +5 °C to +40 °C |
| Surface cross-linking time (MIT 45) | 10-15 minutes |
| Hardening speed | 2-3 mm/24 hours (23 °C – 50% U.R.) |
| Operating temperature | from -25 °C to +80 °C |
| Shore A hardness (ISO 868) | 3 sec. = 36; 15 sec. = 23 |
| Elongation at break (ISO 37 – Type 3) | 110 % |
| Breaking load (ISO 37 – Type 3) | 0,55 N/mm2 |
| 100% elastic modulus (ISO 37 – Type 3) | Type 3 0,5 N/mm2 |
| Elongation at break (UNI EN ISO 8339/A – Mortar substrate – M2) | 20 % |
| Breaking load for traction (UNI EN ISO 8339/A – Mortar support – M2) | 0,15 N/mm2 |
| Maximum working elongation | 7,5 % |
| Withdrawal | -11 ± 2 % |
| Resistance to dripping | Excellent |
| Resistance to diluted acids | Excellent |
| Resistance to bases | Good |
| Resistance to continuous contact with water | Poor |
| Solvent resistance | Poor |
| Resistance to oils and fuels | Poor |
| Paintability | It can be painted with water-based paints. We recommend carrying out preliminary tests. |
| Colour | White |
Indicative yield in linear meters of a sealant cartridge = V / (W x D)
V = Cartridge content in ml
W = Sealing width in mm
D = Sealing depth in mm
Still missing information?